上海特凱焊材工貿(mào)有限公司

MS-2高速鋼模具焊絲

特    性
 含有W Mo Cr V 的高合金焊絲,溶敷金屬具有高韌性,高硬度沖擊耐磨耗性能,可使用在600℃的熱間環(huán)境,焊后金屬可高達HRC61～63度,經(jīng)熱處理后硬度尚有提高. Contains W Mo Cr V high alloy welding wire, soluble deposited metal with high toughness and high hardness, impact abrasion resistance performance can be used in 600 degrees Celsius between thermal environment, after welding metal can be as high as HRC61 ~ 63 degree of hardness, still improve.

 
 
用    途
 焊補冷熱作模具,成型刀具,修整刀具 沖頭 模具 粉碎機刃口,沖壓模具,也可以在碳鋼和低合金鋼上堆焊制成新工具. Heat for mould weld-repair, molding tool, die cutter punch grinder blade, stamping, also can be in the carbon steel and the low alloy steel made on new tools. #